| DuPont Zytel® 135F NC010 Nylon 66 | |||
| Physical Properties物理性质 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Density密度 | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 |
| Water Absorption吸水率 | 2.7 % @Temperature 23.0 °C | 2.7 % @Temperature 73.4 °F | E 50%RH; DAM; ISO 62, Similar to |
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |
| Viscosity粘度 | 55000 cP @Shear Rate 7000 1/s, Temperature 315 °C | 55000 cP @Shear Rate 7000 1/s, Temperature 599 °F | DAM; ISO 11443 |
| 284000 cP @Shear Rate 500 1/s, Temperature 275 °C | 284000 cP @Shear Rate 500 1/s, Temperature 527 °F | DAM; ISO 11443 | |
| Linear Mold Shrinkage, Flow线性收缩率/流动 | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse线性收缩率/横向 | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 |
| Mechanical Properties力学性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Hardness, Rockwell M罗氏硬度M | 64 | 64 | 50%RH; ISO 2039/2 |
| 87 | 87 | DAM; ISO 2039/2 | |
| Hardness, Rockwell R罗氏硬度R | 116 | 116 | 50%RH; ISO 2039/2 |
| 123 | 123 | DAM; ISO 2039/2 | |
| Tensile Strength, Yield屈服拉伸强度 | 67.0 MPa @Temperature 23.0 °C | 9720 psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 96.0 MPa @Temperature 23.0 °C | 13900 psi @Temperature 73.4 °F | DAM; ISO 527 | |
| Elongation at Break断裂伸长率 | 13 % @Temperature 23.0 °C | 13 % @Temperature 73.4 °F | DAM; nominal; ISO 527 |
| 20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |
| Elongation at Yield屈服伸长率 | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 |
| 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | 50%RH; ISO 527 | |
杜邦尼龙树脂135F耐冲击高速脱模